Understanding the Internal Conversion Efficiency of BiVO4/SnO2 Photoanodes for Solar Water Splitting: An Experimental and Computational Analysis
Geronimo, L., Ferreira, C. G., Gacha, V., Raptis, D., Martorell, J., & Ros, C. (2024). Understanding the Internal Conversion Efficiency of BiVO4/SnO2 Photoanodes for Solar Water Splitting: An Experimental and Computational Analysis. ACS Applied Energy Materials, 7(5), 1792–1801. https://doi.org/10.1021/acsaem.3c02775
Abstract
This work aims to understand the spin-coating growth process of BiVO4 photoanodes from a photon absorption and conversion perspective. BiVO4 layers with thicknesses ranging from 7 to 48 nm and the role of a thin (<5 nm) SnO2 hole-blocking layer have been studied. The internal absorbed photon-to-current efficiency (APCE) is found to be nonconstant, following a specific dependence of the internal charge separation and extraction on the increasing thickness. This APCE variation with BiVO4 thickness is key for precise computational simulation of light propagation in BiVO4 based on the transfer matrix method. Results are used for accurate incident photon-to-current efficiency (IPCE) prediction and will help in computational modeling of BiVO4 and other metal oxide photoanodes. This establishes a method to obtain the sample’s thickness by knowing its IPCE, accounting for the change in the internal APCE conversion. Moreover, an improvement in fill factor and photogenerated voltage is attributed to the intermediate SnO2 hole-blocking layer, which was shown to have a negligible optical effect but to enhance charge separation and extraction for the lower energetic wavelengths. A Mott–Schottky analysis was used to confirm a photovoltage shift of 90 mV of the flat-band potential.